Payment & Shipping Terms:
|Material:||Pure Aluminium||Alloy:||1050 1060 1070 1080 1100 1200|
|Thickness:||>0.5mm, < 5.5mm||Diameter:||100mm-1250mm|
|Surface:||Mill Finished Or Coated||Packing:||Strong Pallet|
Alloy: 1*** 3*** 5*** 6*** 8***
Temper: O-H112,T etc.
Surface: Mill Finish
Technology:Hot Rolled & Cold drawn(cast)
Capacity:1500 tons per month
Payment: T/T or L/C at sight
Certificate: SGS/ISO/ROSH/FORM E etc.
Delivery Time :20-35 days after receipt of deposit
Cold Rolling/ Hot Rolling Aluminum Circles are widely used in furnitures like tables. But most aluminum circles clients requested are Deep Drawing Quality Aluminum Circle. These aluminum circle are widely
used in kitchenware, cookware, reflector-light etc.
Aluminum Circle Features:
1. Wide range of selection on circles' size including customized shape and size;
2. Excellent deep drawing and spinning quality;
3. RoHS and REACH compliance.
The properties of aluminum circle for pots, cookware, non-stick aluminium circle (or shaped blanks) make
them ideal for use in a number of markets including the cookware, automotive and lighting industries etc
1. Low anisotropy, which facilitates deep drawing
2. Strong mechanical properties
3. High and homogeneous heat diffusion
4. Ability to be enameled, covered by PTFE (or others), anodized
5. Good reflectivity
6. High strength-to-weight ratio
7. Durability and resistance to corrosion
Aluminum Sheet Processing:
Ingot/Master Alloys--->Melting Furnace--->Holding Furnace--->D.C.Caster--->Slab--->Homogenizing--->Hot Rolling Mill--->Cold Rolling Mill--->Punching--->Annealing Furnace--->Finish Inspection--->Packing--->Delivery
TEMPER THICKNESS(mm) TENSILE STRENGTH ELONGATION% Standard
HO 0.35-10 60-100 ≥ 20 GB/T91-2002
H12 0.5-10 70-120 ≥ 4 GB/T91-2002
H14 0.5-10 85-120 ≥ 2 GB/T91-2002
Aluminum circle Surface Quality
Be free from Oil Stain, Dent, Inclusion, Scratches, Stain, Oxide Discoloration, Breaks, Corrosion, Roll Marks, Dirt Streaks and other defect which will interfere with use.
Aluminum circle Mechanical Property:
Chemical Composite and Mechanical Property could meet the requirements of GB/T, ASTM, ENAW, and JIS Standard
Aluminum circle Packing:
First, plastic cloth with drying agent inside; Second, Pearl Wool; Third, wooden cases with dry agent , fumigation wooden pallets, aluminum surface could cover blue PVC film
Producing Procedure from Aluminum Ingot to Aluminum Circles:
Aluminum Ingot/Master Alloys --- Aluminum Melting Furnace - --- Aluminum Slab --- Hot Rolling (Direct Cast) Or Cold Rolling (Cold Cast) – Punching – Annealing Furnace -- Final Inspection
|Alloy||1050 1060 1100 1200 3003|
|Temper||O, H12, H14, H18 and H24...|
|Diameter||50mm-1600mm, Commonly 200mm to 700mm|
|Lead Time||Within 30-45 days after receiving deposit|
|Packing||Standard Exporting wooden pallets or based on customer requirement|
|Material||Using high-tech machinery utilizing premium grade Aluminum Coil.|
|Surface:||Bright & smooth surface, free from defects like white rust, oil patch, edge damage.|
Deep drawing cookware,
and so on.
Though smelting, casting, hot-rolling, cold-rolling, heat-treatment, finishing and other technology,the heavy melting aluminum and an appropriate quality of alloying elements is processed to light nonferrous metal material which has the characters of fine luster, good looking, light weight, poison less and selflessness, and it also has good properties of transmitting electric current and heat, processing and corrosion-resisting applicability.