Payment & Shipping Terms:
|Material:||Synthetic Cryolite||Sodium As Na:||31 - 34 %|
|Aluminium As Al:||13 - 15 %||Purity As Na3AlF6:||98.0 MIN.|
|Alumina As Al2O3:||1.00 % Max||Ratio NaF / AlF3 By Mass:||1.3 - 1.45|
|Silica As SiO2:||0.20 Max.||Phosphorus As P2O5:||0.01 Max.|
Synthetic Potassium Cryolite K3alf6 Synthetic Cryolite CAS NO. 15096-53-2
Appreciated as the most recommended company, we are engaged in offering Synthetic Cryolite for Abrasive. It is known for its high functionality, compact design and resistance against temperature. As a customer centric organization, we use only quality assured raw material procured from reliable vendors to design the offered product.
• Elegant design
• High strength
• Thermal stability
Cryolite (Na3AlF6, sodium hexafluoroaluminate, sodium aluminium fluoride) is an important raw material for the primary aluminium manufacturing used as a flux to dissolve the alumina in the electrolytical metal extraction. Cryolite is also consumed in the abrasives, ceramics and glass industries.
Fluorsid produces granular cryolite by reacting diluted hydrofluoric acid (HF) and aluminium hydrate (Al(OH)3). The H3AlF6 acid is then converted into sodium salt by ion exchange reaction with a sodium chloride solution. After a solid-liquid separation, the slurry of cryolite is calcined in an internally heated rotary kiln. The final product is in the form of pale pink granules. Milled cryolite is obtained from the granular quality after rotary milling.
Fluorsid's cryolite plant has a production capacity of 20,000 MT/y.
1. As a fluxing agent in aluminum product and non-ferrous metal smelting.
2. As an opacifier and auxiliary solvent in the manufacture of enamel and glass.
3. As a wear- resistant filler for resin and rubber-boned abrasive wheels.
4. Used in the production of ferrous alloy and effervescing steel.
5. As a fusing agent in welding material.
6. As an insecticide of crops, etc.
2.It is colorless monoclinic system crystal
Properties for cryolite:
It is colorless monoclinic system crystal. Non-pure product is greyish white, light yellow, light red or black. M.P.: 1025°C; bulk density: 0.6-1.0g/L, true density: 2.95-3.05g/cm3; specific wt.: 2.75-3.00g/cm3, melting heat: 107KJ; slightly soluble in water, aqueous solution is acidic.
Ingredient First grade
Na% ≥ 32
Ignite on 550oC≤ 3.00
Fineness can be adjusted to meet the needs of customers(-120~-325mesh);
Use for cryolite :
Mainly used as fluxing agent for aluminium electrolysis; also used as anti-wear additive for abrasive products; as flux for iron alloy and rimmed steel, as deoxidizer and residue eliminator for casting, as emulsifying agent for enamel, as opacifier for glass etc.
Packing & Weight for cryolite
In Paper woven bag lined with plastic film, net wt. 25kg, 50kg, 1000kg/bag.
Store in shady and ventilated warehouse.Keep away from kindling and heat source.
Prevent from direct sunlight.Provide with package encapsulation.Deposit separately
from acids and avoid reserving mixedly.
In plastic coating woven bags or woven bags with plastic film inside, 40kgs, 50kgs,or 1000kgs net each, or as per requirement of clients.
|Names||Sodium Aluminum Fluoride, Sodium Hexafluoroaluminate, Ice Spar, Kryolith, Sodium Cryolite, Synthetic Cryolite|
|Loss on drying at 110 ºC||0.20 Max|
|Sodium as Na||31 - 34 %|
|Aluminium as Al||13 - 15 %|
|Purity as Na3AlF6||98.0 MIN.|
|Alumina as Al2O3||1.00 % max|
|Ratio NaF / AlF3 by mass||1.3 - 1.45|
|Silica as SiO2||0.20 Max.|
|Phosphorus as P2O5||0.01 Max.|
|Iron as Fe2O3||0.10 Max.|
|Appearance||An Off white to pinkish tinge granular material|
|Melting Point||1012 ºC|
|Density at 20 ºC||2.85 g/cc|
|Bulk Density||0.9 - 1.2 g/cc|
|Packaging||25 Kg / 50 Kg in HDPE bags with liners. 1 MT in big jumbo bags|
|Safety||Safety precautions & additional information are available in the our MSDS|
|Applications||As an electrolyte in production of Aluminum|
It's mainly used as an adjusting agent for electrolyte in aluminum smelting by fused salt electrolysis, also in ceramic glaze, catalyst and flux of nonferrous metal metallurgy etc.
Though smelting, casting, hot-rolling, cold-rolling, heat-treatment, finishing and other technology,the heavy melting aluminum and an appropriate quality of alloying elements is processed to light nonferrous metal material which has the characters of fine luster, good looking, light weight, poison less and selflessness, and it also has good properties of transmitting electric current and heat, processing and corrosion-resisting applicability.